GSO ASTM C336:2011
Gulf Standard
Current Edition
·
Approved on
12 April 2011
·
Standard Test Method for Annealing Point and Strain Point of Glass by Fiber Elongation
GSO ASTM C336:2011 Files
English
5 Pages
Current Edition
Reference Language
GSO ASTM C336:2011 Scope
1.1 This test method covers the determination of the annealing
point and the strain point of a glass by measuring the
viscous elongation rate of a fiber of the glass under prescribed
condition.
1.2 The annealing and strain points shall be obtained by
following the specified procedure after calibration of the
apparatus using fibers of standard glasses having known
annealing and strain points, such as those specified and
certified by the National Institute of Standards and Technology
(NIST)2 (see Appendix X1).
1.3 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appropriate
safety and health practices and determine the applicability
of regulatory limitations prior to use.
Best Sellers From Construction and Building Sector
GSO 1431:2002
Gulf Technical Regulation
Sanitary appliances - pressurized flushing devices
GSO 1427:2008
Gulf Standard
Ceramic Sanitary Appliances - Western Water Closets
GSO 2084:2010
Gulf Standard
Design and application of speed control humps
GSO 440:2007
Gulf Standard
Calcium Silicate bricks
Recently Published from Construction and Building Sector
GSO EN 933-4:2024
EN 933-4:2008
Gulf Standard
Tests for geometrical properties of aggregates - Part 4: Determination of particle shape - Shape index
GSO ASTM F1861:2024
ASTM F1861:21
Gulf Standard
Standard Specification for Resilient Wall Base
GSO EN 196-3:2024
EN 196-3:2016
Gulf Standard
Methods of testing cement - Part 3: Determination of setting times and soundness
GSO EN 772-11:2024
EN 772-11:2011
Gulf Standard
Methods of test for masonry units - Part 11: Determination of water absorption of aggregate concrete, autoclaved aerated concrete, manufactured stone and natural stone masonry units due to capillary action and the initial rate of water absorption of clay masonry units